Product Attributes:
-
Material: Polyvinyl Chloride (PVC) Moisture Content (%): 0.3%
-
Cycle Times: Over 30 times Flexural Modulus (MPa): 500 MPa
-
Flexural Strength (MPa): 30 MPa Condition After Heating: No bubbles, no cracks, no pinholes
-
Softening Point (℃): 70℃ Dimensional Change Rate After Heating (%): 0.20%
-
Dimensional Change Rate After Heating (%): 0.20% Screw Grip Force at Plate Edge (N): 1070 N
-
Screw Grip Force at Plate Surface (N): 1470 N Single Point Stress (MPa): 700 MPa
-
Repeated Dimensional Change Rate at High and Low Temperature (%): 14.1 mm
Product Specifications:
1. 40*80*3000 (mm), 1.9 Kg/m ±0.1 Kg
2. 50*100*3000 (mm), 3 Kg/m ±0.1 Kg
3. Length can be customized