Name |
PA66 composite |
Spec quantity |
DGK-LFT40 |
|
|
Material Properties |
long fiberLFT reinforced 40% |
Color |
black |
|
|
Sample Status |
pellets |
|||
|
use |
Automotive components, electronic product parts, etc. |
Processing method |
Injection Molding Grade |
|
|
Performance Items |
Test Conditions |
Test Method |
Test data |
unit |
|
Mechanical properties Mechanical Properties |
||||
|
Flexural Strength bending strength |
2mm/min |
GB/T9341 |
282 |
MPa |
|
Flexural Modulus flexural modulus |
2mm/min |
GB/T9341 |
10617 |
MPa |
|
Tensile strength tensile strength |
50mm/min |
GB/T1040 |
228.5 |
MPa |
|
Tensile Modulustensile modulus |
50mm/min |
GB/T1040 |
2081 |
MPa |
|
Elongation at break |
50mm/min |
GB/T1040 |
10 |
% |
|
Unnotched Charpy Impact Simple supported beam without notch impact |
23℃ |
GB/T1043 |
48.2 |
KJ/m2 |
|
Notched Izod impactSimple supported beam notch impact |
23℃ |
GB/T1043 |
10.4 |
KJ/m2 |
|
Notched Izod impact strength Notched impact strength of cantilever bea |
23℃ |
GB/T1843 |
27.8 |
KJ/m2 |
|
Other Properties Others |
||||
|
Melt flow rateMelt Flow Index |
|
GB/T3682-2000 |
22 |
g/10min |
|
densityDensity |
|
GB/T1033-1986 |
1.43 |
g/cm3 |
|
Heat Deflection Temperature Distortion Temperature |
A Method-120℃ |
GB/T1633-2000 |
250 |
℃ |
|
surface resistanceSruface resistance |
|
GB/T1401-2002 |
1014 |
Ω·cm |
|
FlammabilityFlammability |
UL-94 |
GB/T2408-1996 |
HB |
|
|
Injection Molding Process Injection molding process |
Drying temperature |
130 degrees |
Drying time |
4-5 hours |
|
Injection Molding Temperature |
285-295 degrees |
Injection pressure |
75 |
|
|
conclusion (spline size 80*10*4mm) |
The above values and molding processes are laboratory standard values., for reference only, the above process can be adjusted according to different machine models, molds, and product requirements. It does not serve as a guarantee for quality standards or any other purposes. For more details, please contact 0574-62636666. |
|||